PFM923I-6U-C

Conductor

Material

Oxygen free copper (99.97% purity)

Diameter

0.57 mm ± 0.01 mm(0.0224″±0.0004″)

American Wire Gauge

23AWG

Insulation

Material

HDPE

Min. Average Thickness

0.21 mm(0.0082″)

Diameter

1mm±0.05mm(0.0393″±0.0019″)

Color (4 Pairs)

Blue, white/blue; orange, white/orange; green, white/green; brown, white/brown

Separator

Material

PE

Specification

Translucent 4.5 × 0.4 mm

Rip Cord

Material

Polyester

Specification

500D

Sheath

Material

LSZH

Min. Average Thickness

0.43 mm (0.0169″)

Diameter

6.3 mm ± 0.5 mm (0.2480″±0.0196″)

Color

Orange

Electrical

Max. DC Resistance of a Single Conductor

9.38Ω/100 m

Min. Insulation Resistance

5000MΩ·km

Max. DC Resistance Unbalance

≤5%

Dielectric Strength

No breakdown with 1KV DC for 1 min

Transmission

Characteristic Impedance (1-250MHz)

100 ± 15Ω

Mechanical

Tensile Strength

Sheath≥10 MPa, insulation≥16 MPa

Elongation at Break

Sheath≥125%, insulation≥300%

Installation Bending Radius

>8 times of outer cable diameter

Conductor Elongation at Break

≥10%

Environmental

Shrinkage of Insulation

≤5%

Color Migration Resistance of Insulation

No migration

Sheath Tensile Strength and Elongation at Break after Aging

≥8 MPa, ≥100%

Low Temperature Bending Test

No cracking after the test

Heat Shock Test

No cracking after the test

Operation Temperature

–20°C to +60°C (–4°F to 140°F)

Installation Temperature

0°C to +50°C (32°F to 122°F)

Storage Temperature and Humidity

–10°C to +40°C (14°F to 104°F), <60% (RH)

Certification

Certification

CPR Eca